PSI - Issue 3

Francesco Iacoviello et al. / Procedia Structural Integrity 3 (2017) 276–282 Author name / Structural Integrity Procedia 00 (2017) 000–000

282

7

- for the investigated sensitization temperature (800°C) and all the sensitizations times, the intergranular corrosion attack occurs at the same time of the selective attack of the ferritic grains, being this superposition more and more evident with the increase of the sensitization time; - DL-EPR test does not seem to be the best procedure to characterize the intergranular corrosion susceptibility in a steel when a second localized corrosion attack (e.g., ferritic grains selective attack) occurs at the same time.

References

Brandi. S.D., Lippold. J.C., 1997. Considerações sobre a metalurgia da soldagem de aços inoxidáveis duplex e superduplex. Metallurgia & Materiais. 141-146. Charles, J., 2016. Duplex Stainless steels - a Review after DSS '07 held in Grado. Steel Research International. 79, 455-465. Cihal, V., Stefec, R., 2001. On the development of the electrochemical potentiokinetic method. Electrochimica Acta, 46(24-25), 3867-3877. Gunn, R., 1997. Duplex Stainless Steels: Microstructure. Properties and Applications. Woodhead Publishing. Iacoviello. F., Habashi, M., Cavallini, M., 1997. Hydrogen embrittlement in the duplex stainless steel Z2CND2205 hydrogen-charged at 200°C. Mater. Science and Engineering A. A224, 116-124. Iacoviello. F., Boniardi, M., La Vecchia, G.M., 1999. Fatigue crack propagation in austeno-ferritic stainless steel 22 Cr 5 Ni. Int. J. of Fatigue. 21, 957-963. Iacoviello, F., Casari, F., Gialanella, S., 2005. Effect of “475°C embrittlement” on duplex stainless steels localised corrosion resistance. Corrosion Science. 47, 909-922. Josefsson, B., Nilsson, J.O., Wilson, A., 1991. Phase transformations in duplex steels and the relation between continuous cooling and isothermal heat treatment. Duplex Stainless Steel ’91, Beaune, France. 1, 67-78.