as temperature, deformation rate, and processing time, to ensure uniform recrystallization. Based on the current study, the control of strain rate appears to be an effective way to achieve this objective.

5.References

1. Mankinks, W.L., Hosier, J.C., Bassford, T.H., 1974. Microstructure and phase stability of INCONEL 617. Metallurgical Transactions 5, 2579-2590. 2. Divya, M., Dey, H.C., Vasudevan, M., Albert, S.K., 2021. Study on hot-cracking susceptibility of alloy 617M and an analysis on parameters used for its evaluation. Journal of Manufacturing Processes, 68, 1714-1725. 3. Singh, A.N., Moitra, A., Bhaskar, P., Sasikala, G., Dasgupta, A., Bhaduri, A.K.,2018. Effect of thermal aging on microstructure, hardness, tensile and impact properties of alloy 617. Materials Science & Engineering: A, 710, 47-56. 5. Gurianov, D.A., Fortuna, S.V., Osipovich, K.S.,2019. Defects formation features of nickel-based superalloy product obtained by wire feed electron beam additive manufacturing. AIP Conference Proceedings 2167, 020125. 6. Pachala, W., Mazur, A., Jacek, S., Mariusz, K., Sylwia, P., 2011. Effect of Hydrostatic Extrusion with Back Pressure on Mechanical Properties of Grey and Nodular Cast Irons. Archives of Metallurgy and Materials 56, 945-953. 7. Su, Y., Chiang, C.-H., Tsao, C.-Y. A., 2004. Extrusion characteristics of spray-formed AC9A aluminum alloy. Materials Science & Engineering: A 364, 305-312. 8. Onawola,O.O., Adeyemi,M.B, 2003. Warm compression and extrusion tests of aluminium. Journal of Materials Processing Technology136, 7-11. 9. Aashranth, B., Samantaray, D., Davinci, M.A., Murugesan, S., Borah, U., Albert, S.K., Bhaduri, A.K., 2018. A micro-mechanism to explain the post-DRX grain growth at temperatures >0.8Tm. Materials Characterization 136, 100-110. 10. Sperry,R., Harte, A., Fonseca, J.Q., Homer, E.R., Wagoner, R.H., Fullwood, D.T., 2020. Slip band characteristics in the presence of grain boundaries in nickel-based superalloy.Acta Materialia, 193, 229-238. 11. Harte, A., Atkinson, M., Smith, A., Drouven, C., Zaefferer, S., Fonseca, J.Q., Preuss, M., 2020. The effect of solid solution and gamma prime on the deformation modes in Ni-based superalloys. Acta Materialia,194, 257-275. 4. Holdsworth, S.R., 1980. The significance of defects in Ni-base superalloys, Superalloys 1980.