PSI - Issue 10

Alk. Apostolopoulos et al. / Procedia Structural Integrity 10 (2018) 49–58 Alk. Apostolopoulos and T. Matikas / Structural Integrity Procedia 00 (2018) 000 – 000

58 10

 The investigation in combined effect of corrosion phenomena and cyclic loading action leads to useful findings about the response of corroded steel bars under seismic conditions.  Steel bars under corrosive environment and low cycle fatigue conditions present significant degradation to their mechanical performance. References Apostolopoulos, C.A., 2007. Mechanical behavior of corroded reinforcing steel bars S500s tempcore under low cycle fatigue. Construction and Building Materials 21, 1447-1456. Apostolopoulos, C.A., Michalopoulos, D., 2006. Effect of corrosion on mass loss, and high and low cycle fatigue of reinforcing steel. Journal of Materials Engineering and Performance 15, 742-749. Apostolopoulos, C.A., Papadopoulos, M., Pantelakis, Sp.G., 2006. Tensile behavior of corroded reinforcing steel bars BSt 500 S . Construction and Building Materials 20, 782-789. Apostolopoulos, C. et al., 2014. Effects of corrosion on low-cycle fatigue (seismic) behaviour of high strength steel reinforcing bars. RFSR-CT-2009 00023 project. Final report, European Commission, Brussels. Apostolopoulos, Alk., Matikas, T.E, 2016. Corrosion of bare and embedded in concrete steel bar - Impact on mechanical behavior. International Journal of Structural Integrity 7, 240-259. Apostolopoulos, Alk., Matikas, T.E, Kodzhaspirov, G., 2016. Structural integrity of steel bar under seismic loads. Materials Physics and Mechanics 25, 22-29. ASTM Standard B117, 1997. Standard Practice for Operating Slat Spray (Fog) Apparatus. ASTM Intern., West Conshohocken, PA; 2003, doi: 10.1520/B0117-97. Avci, R. et al., 2013. Mechanism of MnS-mediated pit initiation and propagation in carbon steel in an anaerobic sulfidogenic media. Corrosion Science 76, 267-274. Caprili, S., Salvatore, W., 2015. Cyclic behaviour of uncorroded and corroded steel reinforcing bars. Construction and Building Materials 76, 168-186. Clementa, G.G., 2002. Testing of selected metallic reinforcing bars of extending the service life of future concrete bridges, Fin. report, Virginia Transport. , Charlot, VA, Research Council, VTRC 03-A7. El-Bahy, A. et al., 1999. Cumulative seismic damage of circular bridge columns: Benchmark and low-cycle fatigue tests. Journal of ACI Structures 96, 633-643. Hawileh, R.A. et al., 2015. Evaluation of the low-cycle fatigue life in seven steel bar types. ASCE. Journal of Materials in Civil Engineering 28(5), 06015015. ISO/FDIS 15630-1. International Standard. Steel for the reinforcement and prestressing of concrete – test methods. Part 1: reinfor. bars, wire rod and wire; 2002. [ISO/FDIS 15630-1 (2002)]. Jeong, D.Y., Orringen, O., Sih, G.C., 1995. Strain energy density approach to stable crack extension under net section yielding of aircraft fuselage. Journal of Theoretical and Applied Fracture Mechanics 22, 127-137. Kashani, M.M., 2014. Seismic Performance of Corroded RC Bridge Piers: Development of a Multi-Mechanical Nonlinear Fibre Beam-Column Model, PhD Thesis, University of Bristol. Kashani, M.M., Crewe, A.J., Alexander, N.A., 2013a. Nonlinear cyclic response of corrosion damaged reinforcing bars with the effect of buckling. Construction and Building Materials 41, 388-400. Kashani, M.M., Crewe, A.J., Alexander, N.A., 2013b. Nonlinear stress-strain behaviour of Corrosion damaged reinforcing bars including inelastic buckling. Engineering Structures 48, 417-429. Kashani, M.M., Crewe, A.J., Alexander, N.A., 2013c. Use of a 3D optical measurement technique for stochastic corrosion pattern analysis of reinforcing bars subjected to accelerated corrosion. Corrosion Science 73, 208-221. Kashani, M.M. et al., 2014. Finite element investigation of the influence of corrosion pattern on inelastic buckling and cyclic response of corroded reinforcing bars. Engineering Structures 75, 113-125. Kasiraj, I., Yao, J.T.P., 1969. Fatigue damage in seismic structures. Journal of the Structural Division (ASCE) 95, 1673. Krawinkler, H., 1987. Performance assessment of steel components. Earthquake Spectra 3, 27. Lehman, D.E., Moehle, J.P., 2000. Seismic performance of well-confined concrete columns. PEERResearch Report; University of California at Berkeley. Ma, S.Y.M., Bertero, V.V., Popov, E.P., 1976. Experimental and Analytical Studies on the Hysteretic Behaviour of Reinforced Concrete Rectangular and T-Beams. Earthquake Eng. research report 76 (No.2), Berkeley: Univ. of California. Meda, A. et al., 2014. Experimental evaluation of the corrosion influence on the cyclic behaviour of RC columns. Engineering Structures 76, 112-123. Sheng, G.M., Gong, S.H., 1997. Investigation of low cycle fatigue behaviour of building structural steels under earthquake loading. Acta Metallurgica Sinica 10, 51-55. Shigeru, H., 1995. Research report, Retrofitting of reinforced concrete moment Resisting Frames, supervised: Park, R., Tanaka, H., ISSN0110-3326. Sih, G.C., Chao, C.K., 1984. Failure initiation in unnotched specimens subjected to monotonic and cyclic loading. Theoretical and Applied Fracture Mechanics 2, 67-73. Webb, E.G, Paik, C.H, Alkire, R.C., 2001. Local detection of dissolved sulfur species from inclusions in stainless steel using Ag microelectrode. Electrochemical Solid-State Letters 4, B15-B18. Wranglen, G., 1969. Review article on influence of sulphide inclusions on corrodibility of Fe and steel. Corrosion Science 9, 585. Wranglen, G., 1974. Pitting and sulfide inclusions in steel. Corrosion Science 14, 331-349. Yoshaki, T., 1983. Proceedings of Academical Lectures of JAS. Tokyo, 606.