PSI - Issue 68

M. Álvarez et al. / Procedia Structural Integrity 68 (2025) 272–278 M. Álvarez et al. / Structural Integrity Procedia 00 (2025) 000–000

278

7

• S-N curve developed with Bandara et al. (2015) procedure exhibited les conservative estimations than Adasooriya et al. (2020) in the range 300k-10 7 cycles. • Although S-N curves constructed with phenomenological models cannot be used for design purposes, due to the reduced number of experimental points, they provide an acceptable estimate of the S-N fatigue behavior of the corroded material. • This remnant life estimations can be very useful in inspection and repair activities, with a conservatism between experimental data and design codes provided by the codes. References Khodabux W., Causon I., Brennan F. 2020. Profiling corrosion rates for offshore wind turbines with depth in the north sea. Energies, 13, 2518. Han W., Pan C., Wang Z., Yu G. 2014. A study on the initial corrosion behavior of carbon steel exposed to outdoor wet-dry cyclic condition. Corrosion Science, 88, 89-100. Biswal R., Al Mamun A., Mehmanparast A. 2021. On the performance of monopile weldments under service loading conditions and fatigue damage prediction. Fatigue and Fracture of Engineering Materials and Structures, 44, 1469–1483. Jakubowski, M. 2015. Influence of Pitting Corrosion on Fatigue and Corrosion Fatigue of Ship and Offshore Structures, Part II: Load - Pit - Crack Interaction. Polish Maritime Research, 22, 3, 57-66. Liao X., Li Y., Qiang B., Wu J., Yao C., Wei X. 2022. An improved crack growth model of corrosion fatigue for steel in artificial seawater. International Journal of Fatigue, 160, 106882. Álvarez M., Muñiz-Calvente M., Urresti I., Escalero M., Gracia J. 2022. Fatigue life estimation of pre-corroded 42CrMo4 subjected to accelerated pitting corrosion method. International Journal of Fracture, 234, 69–80. Shojai S., Schaumann P., Braun M., Ehlers S. 2022. Influence of pitting corrosion on the fatigue strength of offshore steel structures based on 3D surface scans. International Journal of Fatigue, 164, 107-128. Shamir M., Braithwaite J., Mehmanparast A. 2023. Fatigue life assessment of offshore wind support structures in the presence of corrosion pits. Marine Structures, 92,103505. Morgantini M. 2020. Experimental Investigation of the Combined Effects of Corrosion and Mean Stress on Fatigue Strength of Low Carbon Steel. PhD thesis, University of Strathclyde, Glasgow. Igwemezie V., Mehmanparast A. 2020. Waveform and frecuency effects on corrosion-fatigue crack growth behaviour in modern marine steels. International Journal of Fatigue, 134, 105484. Pargeter R., Baxter D., Holmes B. 2008. Corrosion Fatigue of Steel Catenary Risers in Sweet Production. Proceedings of the ASME 2008 27th International Conference on Offshore Mechanics and Arctic Engineering Volume 3: Pipeline and Riser Technology; Ocean Space Utilization. Estoril, Portugal, 63-74. Palin-Luc T., Pérez-Mora R., Bathias C., Domínguez G., Paris P. C., Arana J. L. 2010. Fatigue crack initiation and growth on a steel in the very high cycle regime with sea water corrosion. Engineering Fracture Mechanics, 77, 11, 1953-1962. British Standards Institution. 2009. Weldable structural steels for fixed offshore structures - Technical delivery conditions (BS EN 10225). Mehmanparast A., Vidament A. 2021 An accelerated corrosion-fatigue testing methodology for offshore wind applications. Engineering Structures, 240, 112414. International Organization for Standardization. 2010. Metallic materials-Tensile testing-Part 1: Method of test at room temperature (ISO 6892-1). International Organization for Standardization. 2009. Metallic materials - Fatigue testing - Axial force-controlled method (ISO 1099). American Society for Testing and Materials. 2020. Standard Test Methods for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys by Use of Ferric Chloride Solution (ASTM G48-1). Gkatzogiannis S., Weinert J., Engelhardt I., Knoedel P., Ummenhofer T. 2019. Correlation of laboratory and real marine corrosion for the investigation of corrosion fatigue behaviour of steel components. International Journal of Fatigue, 126, 90-102. American Society for Testing and Materials. 2021. Standard Practice for Exposure of Metals and Alloys by Alternate Immerion in Neutral 3.5% Sodium Chloride Solution (ASTM G44-21). Det Norske Veritas and Germanischer Lloyd. 2019. Fatigue Design of Offshore Steel Structures (DNVGL-RP-C203). British Standards Institution. 2014. Guide to fatigue design and assessment of steel products (BS 7608:2014). Sonsino C. 2007. Course of SN-curves especially in the high-cycle fatigue regime with regard to component design and safety. International Journal of Fatigue, 29, 2246-2258. Okenyi V., Afazov S., Mansfield N., Eder M. A., Abrahamsen A. B., Faester S., Klingaa C. G., Siegkas P., Bodaghi M. 2023. Corrosion surface morphology-based methodology for fatigue assessment of offshore welded structures. Fatigue and Fracture of Engineering Materials and Structures, 46(12), 4663-4677. Adasooriya N. D., Hemmingsen T., Pavlou D. 2020. Fatigue strength degradation of metals in corrosive environments. IOP Conference Series: Materials Science and Engineering, 43, 721-733. Bandara C. S., Dissanayake U. I., Dissanayake P. B. R.. 2015. Novel method for developing S-N curves for corrosion fatigue damage assessment of steel structures. 6 th International Conference on Structural Engineering and Construction Management, Kandy, Sri Lanka,100-104. Basquin O.H. 1910. The Exponential Law of Endurance Tests. Proceedings of American Society of Testing Materials, 10, 625-630. Mathiesen T., Black A., Grønvold F. 2016. Monitoring and Inspection Options for Evaluating Corrosion in Offshore Wind Foundations. NACE Corrosion 2016, Paper C2016-7702.