Hachimi Taoufik et al. / Procedia Structural Integrity 47 (2023) 711 – 722 Author name / Structural Integrity Procedia 00 (2019) 000 – 000

715

5

Fig. 4. Tensile curve SENT of 0.4 mm thickness (two layers)

Table 2 resumes the results of the uniaxial tensile tests.

Table 2. Result of the tensile test for the 3D-printed ABS 0° 45°

90°

SENT

Young's Modulus (MPa) Elastic limit σ e (MPa) Tensile strength σ m (MPa) Elongation at Break (%)

1080.78

1155.53

1111.03

1016.70

26

28.1 29.2

24.3

22.5

26.08

27.09

24.36

8.2

5.9

3.4

4.4

2.4. Tensile test modeling: The simulation was made for the SENT specimen using software modeling. Operating the quasi-static time independent was defined. They were using the same boundary condition applied to the experiment. The specimens were pinched between the fixed part (encountered) and the loading displacement as the mobile jaws Fig. 5.

Fig. 5. SENT specimen under boundary condition.