Fatigue Crack Paths 2003

Figure 6. 70%AISI 316LHC+ 30%AISI 434 L H C(ρ = 6.89 g/cm3) S E Mfracture surface analysis.

Figure 7. 70%AISI 316LHC+ 30%AISI

434 L H C (ρ = 6.89 g/cm3 optical

microscope fatigue crack path analysis.

Figure 8. 70%AISI 316LHC+ 30%AISI 434 L H C(ρ = 7.12 g/cm3) S E Mfracture surface analysis.

Figure 9. 70%AISI 316LHC+ 30% AISI

434 L H C (ρ = 7.12 g/cm3) optical

microscope fatigue crack path analysis.

Figure 10. 60%AISI 316LHC+ 4 0 %AISI 434 L H C(ρ = 7.14 g/cm3) S E Mfracture surface analysis.

Figure 11. AISI 316LHC+ 40%AISI 434

L H C(ρ = 7.14 g/cm3) optical microscope

fatigue crack path analysis.